SABIC PEEK LL004C沙伯基础--LNP LUBRICOMP LL004C is a compound based on Polyetheretherketone resin containing PTFE. Added features of this material include: Internally Lubricated, Clean Compounding System
Also known as: LNP* LUBRICOMP* Compound LL-4040 CCS
Product reorder name: LL004C
LNP™ LUBRICOMP™ LL004C compound 物性表
基本信息
| 添加剂 |
PTFE润滑剂
|
| 特性 |
Low (to None) Ion Content
润滑
|
物理性能
额定值
单位制
测试方法
| 比重 |
1.37 |
g/cm³ |
ASTM D792, ISO 1183 |
| 收缩率 |
|
|
|
| 流动 : 24小时 |
1.3 |
% |
ASTM D955 |
| 横向流动 : 24小时 |
1.9 |
% |
ASTM D955 |
| 垂直流动方向 : 24小时 |
1.9 |
% |
ISO 294-4 |
| 流动方向 : 24小时 |
1.3 |
% |
ISO 294-4 |
机械性能
额定值
单位制
测试方法
| 拉伸模量 |
|
|
|
| -- 1 |
2900 |
MPa |
ASTM D638 |
| -- |
3070 |
MPa |
ISO 527-2/1 |
| 抗张强度 |
|
|
|
| 屈服 |
74.5 |
MPa |
ASTM D638 |
| 屈服 |
73.0 |
MPa |
ISO 527-2 |
| 断裂 |
69.6 |
MPa |
ASTM D638 |
| 断裂 |
69.0 |
MPa |
ISO 527-2 |
| 伸长率 |
|
|
|
| 屈服 |
5.8 |
% |
ASTM D638 |
| 屈服 |
5.0 |
% |
ISO 527-2 |
| 断裂 |
23 |
% |
ASTM D638 |
| 断裂 |
12 |
% |
ISO 527-2 |
| 弯曲模量 |
|
|
|
| -- |
2960 |
MPa |
ASTM D790 |
| -- |
3320 |
MPa |
ISO 178 |
| 弯曲强度 |
|
|
|
| -- |
117 |
MPa |
ASTM D790 |
| -- |
118 |
MPa |
ISO 178 |
| 摩擦系数 |
|
|
ASTM D3702 Modified |
| 与自身 - 动态 |
0.52 |
|
ASTM D3702 Modified |
| 与自身 - 静态 |
0.43 |
|
ASTM D3702 Modified |
| 磨损因数 - Washer |
128 |
10^-10 in^5-min/ft-lb-hr |
ASTM D3702 Modified |
冲击性能
额定值
单位制
测试方法
| 悬壁梁缺口冲击强度 |
|
|
|
| 23°C |
96 |
J/m |
ASTM D256 |
| 23°C 2 |
8.8 |
kJ/m² |
ISO 180/1A |
| 无缺口悬臂梁冲击 |
|
|
|
| 23°C |
1500 |
J/m |
ASTM D4812 |
| 23°C 3 |
91 |
kJ/m² |
ISO 180/1U |
| 装有测量仪表的落镖冲击 |
|
|
|
| 23°C, Energy at Peak Load |
3.00 |
J |
ASTM D3763 |
| -- |
1.00 |
J |
ISO 6603-2 |