沙伯基础LC-1006属于聚醚醚酮碳纤维增强材料,聚合物,热塑性塑料,聚酮,聚醚醚酮(PEEK),聚醚酮,PEEK,碳纤维填充
Forms: Pellets
Processing Method: Injection Molding
Information provided by LNP, a GE Plastics Company.
This data sheet is labeled Discontinued; however many LNP grades are still active under new names instituted after the SABIC purchase
LNP Thermocomp® LC-1006 Polyetheretherketone, Carbon Fiber Reinforcement 物性表
比重 | 1.41 g/cc | 1.41 g/cc | Method A; ASTM D792 |
线性成型收缩率 | 0.0010 cm/cm | 0.0010 in/in | ASTM D955 |
线性成型收缩率,横向 | 0.0040 cm/cm | 0.0040 in/in | ASTM D955 |
抗张强度(断裂) | 225 MPa | 32600 psi | ASTM D638 |
抗张强度(屈服) | 225 MPa | 32600 psi | ASTM D638 |
伸长率 (断裂) | 1.5 % | 1.5 % | ASTM D638 |
屈服伸长率 | 1.4 % | 1.4 % | ASTM D638 |
拉伸模量 | 30.8 GPa | 4470 ksi | ASTM D638 |
弯曲强度 | 324 MPa | 47000 psi | ASTM D790 |
弯曲模量 | 20.2 GPa | 2930 ksi | ASTM D790 |
悬壁梁缺口冲击强度 | 0.747 J/cm
@Thickness 3.18 mm
|
1.40 ft-lb/in
@Thickness 0.125 in
|
ASTM D256 |
悬壁梁无缺口冲击强度 | 6.09 J/cm
@Thickness 3.18 mm
|
11.4 ft-lb/in
@Thickness 0.125 in
|
ASTM D256 |
悬壁梁缺口冲击强度 | 7.80 kJ/m² | 3.71 ft-lb/in² | ISO 180 |
悬壁梁无缺口冲击强度 | 42.6 kJ/m² | 20.3 ft-lb/in² | ISO 180 |
Falling Dart Impact | 12.5 J | 9.22 ft-lb | ASTM D3763 |
动态摩擦系数 | 0.30 | 0.30 | vs. Steel - @ 40 psi, 50 ft/min, tested in accordance with LNP WI-0687; ASTM D1894 |
静态摩擦系数 | 0.32 | 0.32 | vs. Steel @ 40 psi, tested in accordance with LNP WI-0687; ASTM D1894 |
K (wear) Factor | 111 x 10-8 mm³/N-M | 55.0 x 10-10 in³-min/ft-lb-hr | 40psi, 50ft/min; tested in accordance with LNP WI-0687 |
线性热膨胀系数 | 11.0 µm/m-°C
@Temperature 20.0 °C
|
6.11 µin/in-°F
@Temperature 68.0 °F
|
TMA; ASTM E831 |
线性热膨胀系数,横向流动 | 29.0 µm/m-°C
@Temperature 20.0 °C
|
16.1 µin/in-°F
@Temperature 68.0 °F
|
TMA; ASTM E831 |
载荷下热变形温度(0.46 MPa) | 299 °C | 570 °F | Unannealed; ASTM D648 |
载荷下热变形温度(1.8 MPa) | 299 °C | 570 °F | Unannealed; ASTM D648 |
可燃性(UL94) | V-0
@Thickness 0.770 mm
|
V-0
@Thickness 0.0303 in
|
加工(熔体)温度 | 379 - 388 °C | 714 - 730 °F | |
模具温度 | 135 - 163 °C | 275 - 325 °F | |
干燥温度 | 121 - 149 °C | 250 - 300 °F | |
干燥时间 | 4 hour | 4 hour | |
水分含量 | 0.10 % | 0.10 % | Suggested |
背压 | 0.345 - 0.689 MPa | 50.0 - 99.9 psi |