HIC试验和SSCC试验有关内容
序号
|
评定编号
|
材质
|
厚度
|
焊接方法
|
1
|
PS2012-48
|
Q345R(R-HIC)
|
δ=8
|
SMAW:DC-
|
2
|
PS2012-49
|
Q345R(R-HIC)
|
δ=8
|
GTAW:DC+
|
3
|
PS2012-50
|
Q345R(R-HIC)
|
δ=16
|
GTAW:DC+
SMAW:DC- |
4
|
PS2012-51
|
Q345R(R-HIC)
|
δ=38
|
SAW:DC-
|
5
|
PS2012-52
|
Q345R(R-HIC)
|
δ=38
|
SMAW:DC-
|
6
|
PS2012-53
|
Q345R(R-HIC)
|
δ=4
|
GTAW:DC+
|
7
|
PS2012-54
|
Q345R(R-HIC)
|
δ=10
|
SAW:DC-
|
8
|
PS2012-55
|
Q245R(R-HIC)
|
δ=8
|
SMAW:DC-
|
9
|
PS2012-56
|
Q245R(R-HIC)
|
δ=4
|
SMAW:DC-
|
10
|
PS2012-57
|
Q345R(R-HIC)
|
δ=4
|
SMAW:DC-
|
1.熔敷金属进行抗氢致开裂(HIC)试验
GB/T8650-2015《管线钢和压力容器钢抗氢致开裂评定方法》A溶液 CLR≤15% CTR≤5% CSR≤2%
2. 熔敷金属进行抗硫化物应力开裂(SSCC)试验
GB/T4157-2017《金属在硫化氢环境中抗特殊形式环境开裂实验室试验》A溶液,试验加载应力≥80%SMYS,试验时间720小时,合格级别标准中9.7.1(b)规定c