Polyplastics
分类 | | | 特长 | | | 品级 | | | 颜色 | | | UL94 | |
| | 非增强 | | | 高韧性 | | | 0220A9 | | | HD9100 | | | V-0 | |
| | 玻璃纤维增强 | | | 标准, 低溢料 | | | 1130A64 | | ||
| | 1140A64 | | | HF2000/HD9100 | | |||
| | 低翘曲, 低溢料 | | | 1150A64 | | | HD9050 | | ||
| | 超高流动性·低溢料 | | | 1140A7 | | | HF2000/HD9050 | | ||
| | 高强度 | | | 1140A6 | | |||
| | 高韧性 | | | 1130A1 | | |||
| | 1140A1 | | ||||
| | 低溶出性 | | | 1140A65 | | | HF2000 | | ||
| | 低氯 | | | 1140A66 | | |||
| | 玻璃纤维增强/无机物增强 | | | 尺寸精度优良·标准 | | | 6165A4 | | | HF2000/HD9050/HD9100 | | |
| | 6165A6 | | ||||
| | 尺寸精度优良·低溢料 | | | 6165A7 | | |||
| | 低翘曲·外观良好 | | | 6465A6 | | |||
| | 6465A62 | | ||||
| | 低温模具·良好树脂间粘接性 | | | 6565A6 | | |||
| | 6565A7 | | ||||
| | | | | 6165A7S | | | - | | ||
| | 特殊 | | | 高耐冲击 | | | 0220U9 | | ||
| | 1130T6 | | | V-0 (1.6mm) | | |||
| | 6150T6 | | ||||
| | 滑动性 | | | 3130A1 | | |||
| | 6345A4 | | ||||
| | 导电性·滑动性 | | | 2130A1 | | | HD9000 | | ||
| | 7140A4 | | ||||
| | 导电性 | | | 7340A4 | | | V-1 | |
PPS(聚苯硫醚#)/1301-7971/德国雷曼福斯
用途： 汽车部件, 医用
特性备注：导热 低翘曲性 刚性，良好 良好的强度
重要参数： 密度:2.12 g/cm3 吸水率:0.05 % 成型收缩率:0.3 % 缺口冲击强度:9 弯曲强度:105 MPa 弯曲模量:9000 MPa
生产厂商：德国雷曼福斯公司
PPS(聚苯硫醚#)/1301-8312/德国雷曼福斯
重要参数： 密度:1.65 g/cm3 吸水率:0.05 % 成型收缩率:0.3 % 缺口冲击强度:4 弯曲强度:72 MPa 弯曲模量:12000 MPa
PPS(聚苯硫醚#)/1301-8331/德国雷曼福斯
重要参数： 密度:1.75 g/cm3 吸水率:0.05 % 成型收缩率:0.2 % 缺口冲击强度:5 弯曲强度:100 MPa 弯曲模量:20000 MPa
PPS(聚苯硫醚#)/GK/400/意大利拉题
用途： 其它
特性备注：耐化学性良好 耐热性，高
重要参数： 密度:1.59 g/cm3 成型收缩率:0.1 % 缺口冲击强度:55 维卡软化点:260 ℃ 热变形温度:280 ℃
供应 Polyplastics PPS 1140A6 BK 价格
生产厂商：意大利拉题公司
折叠加工方法
(1)注塑:可采用通用注塑机，玻璃纤维增强PPS的熔融指数以50为宜。注塑的工艺条件为:料筒温度，纯PPS为280~330℃，40%GFPPS为300-350℃;喷嘴温度，纯PPS为305℃，40%GFPPS为330℃;模具温度120-180℃;注塑压力，50-130MPA。
(2)挤出:采用排气式挤出机，工艺为:加料段温度小于200℃;料筒温度300-340℃，连接体温度320-340℃，口模温度300-320℃
。
(3)模压成型:适合大型制品，采用两次压缩，先冷却，后热压。热压的预热温度纯PPS为360℃左右15min,GFPPS为380℃左右20min;模压压力为10~30Mpa，冷却到150℃脱模。
(4)喷涂成型:采用悬浮喷涂法和悬浮喷涂与干粉热喷混合法，都是将PPS喷涂到金属表面，再经过塑化、淬火处理而得到涂层;PPS的涂层处理温度在300℃以上，保温30min。
牌PPS1140A6）总代理商