现货美国伊士曼TX2001不含双酚A食品级PCTG共聚聚酯,高透明度、耐冲击、耐化学性好、高耐热(HDT)109℃,抗刮花性。该共聚聚酯材料已经获得了世界上主要国家和地区的食品接触材料产品使用许可,包括美国、欧洲、加拿大和日本,此外,它也获得了中国的使用许可。
伊士曼TX2001带COA出厂证明出货,资料齐全,物性数据如下:
Physical | Nominal Value | Unit | Test Method |
Density / Specific Gravity | 1.17 | g/cm³ | ASTM D792 |
Molding Shrinkage - Flow | 0.50 to 0.70 | % | ASTM D955 |
Mechanical | Nominal Value | Unit | Test Method |
Tensile Modulus (23°C) | 1590 | MPa | ASTM D638 |
Tensile Modulus (23°C) | 1620 | MPa | ISO 527-1 |
Tensile Strength (Yield, 23°C) | 44 | MPa | ASTM D638 |
Tensile Stress (Yield, 23°C) | 45 | MPa | ISO 527-2 |
Tensile Strength (Break, 23°C) | 53 | MPa | ASTM D638 |
Tensile Stress (Break, 23°C) | 49 | MPa | ISO 527-2 |
Tensile Elongation (Yield, 23°C) | 7 | % | ASTM D638 |
Tensile Strain (Yield, 23°C) | 7 | % | ISO 527-2 |
Tensile Elongation (Break, 23°C) | 140 | % | ASTM D638 |
Tensile Strain (Break, 23°C) | 130 | % | ISO 527-2 |
Flexural Modulus (23°C) | 1590 | MPa | ASTM D790 |
Flexural Modulus (23°C) | 1530 | MPa | ISO 178 |
Flexural Strength (Yield, 23°C) | 66 | MPa | ASTM D790 |
Impact | Nominal Value | Unit | Test Method |
Notched Izod Impact (23°C) | 650 | J/m | ASTM D256 |
Notched Izod Impact Strength | ISO 180 | ||
-40°C | 14 | kJ/m² | |
23°C | 66 | kJ/m² | |
Unnotched Izod Impact (23°C) | No Break | ASTM D4812 | |
Hardness | Nominal Value | Unit | Test Method |
Rockwell Hardness (R-Scale, 23°C) | 115 | ASTM D785 | |
Thermal | Nominal Value | Unit | Test Method |
Deflection Temperature Under Load (0.45 MPa, Unannealed) | 109 | °C | ASTM D648 |
Deflection Temperature Under Load (1.8 MPa, Unannealed) | 92 | °C | ASTM D648 |
Optical | Nominal Value | Unit | Test Method |
Light Transmittance (Total) | 92 | % | ASTM D1003 |
Haze | < 1.00 | % | ASTM D1003 |