熔体流动速率 | 7.1 | g/10min | ASTM D-1238 |
弯曲模量 | 9450 | kg/cm | ASTM D-790 |
拉伸屈服强度 | 280 | kg/cm | ASTM D-638 |
IZOD冲击强度 (23℃) | 7 | kg.cm/cm | ASTM D-256 |
断裂伸长率 | 500 | % | ASTM D-638 |
洛氏硬度 | 64 | R标尺 | ASTM D-785 |
维卡软化点 | 130 | ℃ | ASTM D-1525 |
热变形温度 (4.6kg/cm) | 90 | ℃ | ASTM D-648 |
熔体流动速率 | 7.1 | g/10min | ASTM D-1238 |
弯曲模量 | 9450 | kg/cm | ASTM D-790 |
拉伸屈服强度 | 280 | kg/cm | ASTM D-638 |
IZOD冲击强度 (23℃) | 7 | kg.cm/cm | ASTM D-256 |
断裂伸长率 | 500 | % | ASTM D-638 |
洛氏硬度 | 64 | R标尺 | ASTM D-785 |
维卡软化点 | 130 | ℃ | ASTM D-1525 |
热变形温度 (4.6kg/cm) | 90 | ℃ | ASTM D-648 |