密度 | 862 | kg/m | ASTM D1505 |
表面硬度 | 56 | Shore A | ASTM D2240 |
拉伸强度 | >3 | MPa | ASTM D638 |
断裂伸长率 | >800 | % | ASTM D638 |
熔点 | <50 | ℃ | ASTM D2117 |
熔融指数 (190℃) | 3.6 | g/10min | ASTM D1238 |
维卡软化点 | -- | ℃ | ASTM D1525 |
脆化温度 | <-70 | ℃ | ASTM D746 |
密度 | 862 | kg/m | ASTM D1505 |
表面硬度 | 56 | Shore A | ASTM D2240 |
拉伸强度 | >3 | MPa | ASTM D638 |
断裂伸长率 | >800 | % | ASTM D638 |
熔点 | <50 | ℃ | ASTM D2117 |
熔融指数 (190℃) | 3.6 | g/10min | ASTM D1238 |
维卡软化点 | -- | ℃ | ASTM D1525 |
脆化温度 | <-70 | ℃ | ASTM D746 |