物性纠错
物理性能测试条件测试方法测试结果单位密度 / 比重ASTM D-792无水｜1.59
ASTM D-7921.3%水｜-
23°Cg/cm³1.59--收缩率TD:3.00mm3%0.60到0.90--MD:3.00mm4%0.20到0.50--吸水率23°C,24hr%0.60--饱和,23°C%4.0--机械性能测试条件测试方法测试结果单位拉伸应力-40°CMPa190--23°CMPa165
80°CMPa110--抗拉断裂强度23℃ASTM D-638无水｜1640kg/cm223℃ASTM D-6381.3%水｜1350kg/cm2断裂伸长率23℃ASTM D-638无水｜5%23℃ASTM D-6381.3%水｜5%挠曲强度23℃ASTM D-790无水｜2490kg/cm223℃ASTM D-7901.3%水｜2000kg/cm2挠曲模量23℃ASTM D-790无水｜93200kg/cm223℃ASTM D-7901.3%水｜65000kg/cm2拉伸应变断裂,-40°C%2.5--断裂,23°C%3.03.0断裂,80°C%4.5--弯曲模量-40°CMPa10200--23°CMPa9300650080°CMPa5500--弯曲应力-40°CMPa275--23°CMPa250
80°CMPa150--泰伯耐磨性1000Cyclesmg26.0--IZOD冲击强度23℃，无缺口1/8
无水｜65kg.cm/cm23℃，无缺口1/8
1.3%水｜70kg.cm/cm热性能测试条件测试方法测试结果单位热变形温度0.45MPa,未退火°C251--熔融温度
°C265--线形热膨胀系数MDcm/cm/°C2E-05--线性热膨胀系数
ASTM D-696无水｜210-5cm/cm.℃
ASTM D-6961.3%水｜-
热挠曲温度18.6kg/cm2ASTM D-648无水｜251°C18.6kg/cm2ASTM D-6481.3%水｜-°C熔点
差示扫描测热计DSC法无水｜265°C
差示扫描测热计DSC法1.3%水｜-°CUL-94抗燃级
UL 94无水｜V-0
UL 941.3%水｜-
电气性能测试条件测试方法测试结果单位体积电阻率
ASTM D-257无水｜8×1014Ω.cm
ASTM D-2571.3%水｜8×1013Ω.cm介电强度1/8"ASTM D-149无水｜38KV/mm1/8"ASTM D-1491.3%水｜33KV/mmIEC导电径迹指数
UL 746无水｜200V
UL 7461.3%水｜-V损耗因数106HzASTM D-150无水｜0.003-0.009
106HzASTM D-1501.3%水｜-
抗电弧性1/8"ASTM D-495无水｜70-80S1/8"ASTM D-4951.3%水｜-S体积电阻率
ohms·cm1E+151E+13介电强度
kV/mm3833介电常数523°C,1kHz
4.00--23°C,1MHz
0.0100--耐电弧性6
sec70.0--相比耐漏电起痕指数CTIV200--冲击性能测试条件测试方法测试结果单位简支梁缺口冲击强度-40°CkJ/m²7.0--23°CkJ/m²9.514简支梁无缺口冲击强度23°CkJ/m²6570硬度测试条件测试方法测试结果单位洛氏硬度R计秤,23°C
121--其它性能测试条件测试方法测试结果单位强化含量
无水｜30wt%
1.3%水｜-wt%可燃性测试条件测试方法测试结果单位UL阻燃等级0.40mm
V-0--基本性能测试条件测试方法测试结果单位吸水率23℃，24小时ASTM D-570无水｜0.4%23℃，24小时ASTM D-5701.3%水｜-%