静电耗散导电型尼龙碳纤增强塑料,静电耗散尼龙,导电尼龙,导电碳纤尼龙
主要物性数据:
PERMANENCE | English | SI Metric | ASTM TEST |
||
Primary Additive | 25 % | 25 % | |||
Specific Gravity | 1.32 | 1.32 | D 792 | ||
Molding Shrinkage | |||||
1/8 in (3.2 mm) section | 0.0030 - 0.0050 in/in | 0.30 - 0.50 % | D 955 | ||
MECHANICAL |
|||||
Impact Strength, Izod | |||||
notched 1/8 in (3.2 mm) section | 2.5 ft-lbs/in | 133 J/m | D 256 | ||
unnotched 1/8 in (3.2 mm) section | 15.0 ft-lbs/in | 801 J/m | D 4812 | ||
Tensile Strength | 15000 psi | 103 MPa | D 638 | ||
Tensile Elongation | 2.0 - 4.0 % | 2.0 - 4.0 % | D 638 | ||
Tensile Modulus | 1.10 x 10^6 psi | 7584 MPa | D 638 | ||
Flexural Strength | 24000 psi | 165 MPa | D 790 | ||
Flexural Modulus | 0.95 x 10^6 psi | 6550 MPa | D 790 | ||
ELECTRICAL |
|||||
Volume Resistivity | 1000 - 9.9E+09 ohm.cm | 1000 - 9.9E+09 ohm.cm | D 257 | ||
Surface Resistivity | 1.0E+5 - 9.9E+11 ohm/sq | 1.0E+5 - 9.9E+11 ohm/sq | D 257 ESD STM11.11 |
||
Surface Resistance | 1.0E+4 - 9.9E+10 ohm | 1.0E+4 - 9.9E+10 ohm | ESD STM11.11 | ||
Static Decay | |||||
MIL-PRF-81705D, 5kV to 50 V, 12% RH | < 2.00 s | < 2.00 s | FTMS101C 4046.1 |
静电耗散导电型尼龙碳纤增强塑料,静电耗散尼龙,导电尼龙,导电碳纤尼龙
静电耗散导电型尼龙碳纤增强塑料,静电耗散尼龙,导电尼龙,导电碳纤尼龙
其他常有的型号:
RTP 200 H SI 2 Silicone 2%
RTP 283 H Carbon Fiber 20%
RTP 285 H Carbon Fiber 30%
RTP 287 H Carbon Fiber 40%
PermaStat® 200 H Permanently Anti-static/All Polymeric
ESD A 200 H Static Dissipative
ESD A 204 H Static Dissipative - Glass Fiber 25%
ESD C 200 H Electrically Conductive
ESD C 202 H Electrically Conductive - Glass Fiber 15%
ESD C 203 H Electrically Conductive - Glass Fiber 20%
ESD C 204 H Electrically Conductive - Glass Fiber 25%
ESD C 280 H Electrically Conductive - Carbon Fiber
EMI 261 H EMI/RFI Shielding - Stainless Steel Fiber 10%
静电耗散导电型尼龙碳纤增强塑料,静电耗散尼龙,导电尼龙,导电碳纤尼龙加工参数:
GENERAL PROCESSING FOR INJECTION MOLDING | |||||
English | SI Metric | ||||
Injection Pressure | 10000 - 18000 psi | 69 - 124 MPa | |||
Melt Temperature | 530 - 570 °F | 277 - 299 °C | |||
Mold Temperature | 150 - 225 °F | 66 - 107 °C | |||
Drying | 4 hrs @ 175 °F | 4 hrs @ 79 °C | |||
Moisture Content | 0.20 % | 0.20 % | |||
Dew Point | 0 °F | -18 °C | |