密度 | ASTM D792/ISO 1183 | 0.935 | ||
熔融指数(流动系数) | ASTM D1238/ISO 1133 | 5 | g/10min |
ESCR | ASTM D-1693A | >300 | hrs |
弯曲强度 | ASTM D-790 | 19.3 | Mpa | |
拉伸断裂强度 | ASTM D-638 | 11.5 | % | |
伸长率 | 断裂 | ASTM D-638 | 700 | % |
1%割线模量 | ASTM D-790 | 500 | Mpa | |
拉伸屈服强度 | ASTM D-638 | 18 | Mpa | |
硬度 | ASTM D-2240 | 69 | ||
弯曲模量 | ASTM D-790 | 724 | Mpa | |
断裂伸长率 | ASTM D638/ISO 527 | 700 | % | |
拉伸模量 | ASTM D638/ISO 527 | 19.3 | kg/cm²(MPa)[Lb/in²] | |
拉伸强度 | ASTM D638/ISO 527 | 18 | kg/cm²(MPa)[Lb/in²] | |
弯曲模量 | ASTM D790/ISO 178 | 724 | kg/cm²(MPa)[Lb/in²] |