物性表
密度 / 比重 | ASTMD792 | 1.04 | g/cm³ | |
表观密度 | ASTMD1895 | 0.65 | g/cm³ | |
熔体质量流动速率 | 200°C/5.0kg | ASTMD1238 | 10 | g/10min |
拉伸模量3 | 3.20mm | ASTMD638 | 3250 | Mpa |
抗张强度3 | 3.20mm | ASTMD638 | 45.0 | Mpa |
伸长率3 | 断裂,3.20mm | ASTMD638 | 1.8 | % |
弯曲模量 | 3.20mm | ASTMD790 | 3200 | Mpa |
弯曲强度 | 3.20mm | ASTMD790 | 80.0 | Mpa |
热变形温度 | 1.8MPa,未退火,12.7mm | ASTMD648 | 84.0 | °C |
维卡软化温度 | -- | ASTMD15254 | 95.0 | °C |
维卡软化温度 | -- | ASTMD15255 | 90.0 | °C |
悬壁梁缺口冲击强度 | 23°C,3.20mm | ASTMD256 | 13 | J/m |