物性表
密度 / 比重 | ASTM D-792 | 1.04 |
拉伸强度 | ASTM D-638 | 42 | Mpa | |
弯曲强度 | ASTM D-790 | 80 | Mpa | |
弯曲模量 | ASTM D-790 | 3200 | Mpa |
维卡软化点 | ASTM D-1525 | 95 | °C |
成型方法 | Method | 注塑 |
单体残余量 | GasChrom | 600 | ppm |
熔融指数 | ASTM D-1238 | 8.0 | g/10min |
密度 / 比重 | ASTM D-792 | 1.04 |
拉伸强度 | ASTM D-638 | 42 | Mpa | |
弯曲强度 | ASTM D-790 | 80 | Mpa | |
弯曲模量 | ASTM D-790 | 3200 | Mpa |
维卡软化点 | ASTM D-1525 | 95 | °C |
成型方法 | Method | 注塑 |
单体残余量 | GasChrom | 600 | ppm |
熔融指数 | ASTM D-1238 | 8.0 | g/10min |