汽车座椅SPFH780宝钢酸洗加工配送

手机版链接：https://m.trustexporter.com/cz4811141.htm
 Q/BQB 310－2018 4 表 2 牌号 化学成分 a（质量分数） ％ C Si Mn P S Alt SAPH310 ≤0.10 ≤0.30 ≤0.80 ≤0.025 ≤0.020 ≥0.010 SAPH370 ≤0.21 ≤0.30 ≤1.00 SAPH400 ≤0.21 ≤0.30 ≤1.40 ≤0.025 ≤0.020 SAPH440 ≤1.60 SPFH540 ≤0.15 ≤0.50 ≤1.80 SPFH590 ≤0.18 ≤0.60 ≤2.00 ≤0.025 ≤0.020 SPFH780 ≤0.20 ≤1.00 ≤2.10 B440QK ≤0.21 ≤0.35 ≤1.80 ≤0.025 ≤0.020 B330CL ≤0.10 ≤0.30 ≤0.80 B380CL ≤0.12 ≤0.30 ≤1.50 ≤0.025 ≤0.020 B420CL ≤0.12 ≤0.30 ≤1.50 B450CL ≤0.10 ≤0.30 ≤1.50 ≤0.025 ≤0.020 B500CL ≤0.12 ≤0.30 ≤1.60 ≤0.025 ≤0.020 B530CL ≤0.12 ≤0.30 ≤1.60 ≤0.025 ≤0.020 B550CL ≤0.12 ≤0.30 ≤2.00 ≤0.025 ≤0.020 B600CL ≤0.15 ≤0.30 ≤2.00 ≤0.025 ≤0.020 B650CL ≤0.15 ≤0.50 ≤2.00 ≤0.025 ≤0.020 B320L ≤0.10 ≤0.30 ≤0.80 ≤0.025 ≤0.020 B420L ≤0.12 ≤0.50 ≤1.50 ≤0.020 B510L ≤0.16 ≤0.50 ≤1.60 ≤0.020 B510DL ≤0.18 ≤0.30 ≤1.60 ≤0.025 ≤0.020 B550L ≤0.16 ≤0.50 ≤1.60 ≤0.025 ≤0.020 B440QZR ≤0.12 ≤0.50 ≤1.30 ≤0.025 ≤0.020 － B480QZR ≤0.16 ≤0.50 ≤1.50 ≤0.020 a 为改善钢的性能，根据需要可添加其他合金元素，此时 Alt 的下限不要求。 表 3 牌号 化学成分 a（质量分数） ％ C Si Mn P S Alt 其他 QStE340TM ≤0.12 ≤0.50 ≤1.30 ≤0.025 ≤0.020 ≥0.015 Nb≤0.09 V≤0.20 Ti≤0.15 QStE380TM ≤1.40 QStE420TM ≤1.50 QStE460TM ≤1.60 QStE500TM ≤1.70 a 为改善钢的性能，根据需要可添加 Nb、V、Ti 中一种或几种合金元素，但 Nb+V+Ti≤0.22%。
Q/BQB 310－2018 5 表 4 牌号 化学成分 a （质量分数） ％ C Mn Si P S Alt Nba V a Tia Mo B QStE550TM B610L(B600L) ≤0.12 ≤1.80 ≤0.50 ≤0.025 ≤0.015 ≥0.015 ≤0.09 ≤0.20 ≤0.15 － － QStE600TM B650L ≤0.12 ≤1.90 ≤0.50 ≤0.025 ≤0.015 ≥0.015 ≤0.09 ≤0.20 ≤0.22 ≤0.50 ≤0.005 QStE650TM B700L ≤0.12 ≤2.00 ≤0.60 ≤0.025 ≤0.015 ≥0.015 ≤0.09 ≤0.20 ≤0.22 ≤0.50 ≤0.005 QStE700TM B750L ≤0.12 ≤2.10 ≤0.60 ≤0.025 ≤0.015 ≥0.015 ≤0.09 ≤0.20 ≤0.22 ≤0.50 ≤0.005 a 钢中可添加 Nb、V、Ti 中一种或几种合金元素，但 Nb+V+Ti≤0.22。 6.5 力学和工艺性能 6.5.1 钢板及钢带的力学和工艺性能应符合相应表 5～表 10 的规定。 6.5.2 弯曲试验后，试样的外表面不得有肉眼可见的裂纹。供方如能保证弯曲试验合格，可不进行试 验。 6.6 表面质量 6.6.1 钢板及钢带表面不得有裂纹、结疤、折叠、气泡和夹杂等对使用有害的缺陷，钢板及钢带不得 有分层。对酸洗表面的钢板及钢带不得有停车斑。 6.6.2 钢板及钢带按表面质量分为二级，如表 11 示。 6.6.3 对于钢带，由于没有机会切除带缺陷部分，所以钢带允许带有缺陷交货，但有缺陷的部分不得 超过每卷总长度的 5％。 表 5 牌号 拉伸试验 a 1800弯曲试验 b